126M3Sジルコンマット(1.8L) 色:Achromatic (white, black, gray) - Glaze cracking or shrinkage

- Glaze cracking or shrinkage <br>If dust

Soil type: Porcelain and pottery possible Firing method: Oxidation and reduction possible

ですので、ホコリ・汚れ・素焼きの粉や手の脂が付かぬようにご注意ください。

焼き物を作る時に使用するロクロをアメカジ風にアレンジしました。

深海商店の呉須は製造開始から完成まで1ヶ月以上かけております。

126M3Sジルコンマット(1.8L) 色:Achromatic (white, black, gray) - Glaze cracking or shrinkage[Firing conditions for sample plates] Clay components For pottery: Umezaki red clay (SiO2 72. 11%, Al2O3 15. 98%, Fe2O3 2. 12%, TiO2 0. 67%, CaO 0. 12%, MgO 0. 36%, Na2O 0. 58%, K2O 2. 47%, Ig. Loss 5. 16%) Firing temperature : Reduction: 1280 Oxidation: 1230 Glazing : Baume concentration 50 (soak for about 3 seconds) [How to use] Soil type: porcelain, pottery Possible firing method: oxidation and reduction possible Appropriate firing temperature: